Item NO.:
JLY-ZM50Application:
As rheological agent for ink,patint&coatingSolid Content:
50%Clour:
Transparent with light yellow liquidSolvent:
Water or environmental hydrophilic solventDescription:
JLY-ZM50 is a polyether type polyurethane associative thickener(rheological agent) with medium shear viscosity. It exhibits high viscosity at low shearing rates and good pseudoplasticity, as well as excellent flowability. It is used in coloring systems, and its excellent dispersive properties help to wet and disperse pigments in the formulation, resulting in a uniformly rich and full-bodied coating without affecting gloss condition
Application
Such as water-based synthetic leather, water-based coatings, water-based adhesives, etc. CombiningJLY-ZM50 with cellulose ether types or polyacrylic acid types of thickeners can provide the coating with better flowability and anti-splash properties. It can resist microbial degradation and its thickening capacity depends on the structure, particle size, and emulsifier of the latex as well as the film-forming agents and surfactants in the coating.
Technical Data
|
Item |
JLY-ZM50 |
|
Appearance |
Transparent with light yellow liquid |
|
Solid Content (%) |
50±1（150℃，45min） |
|
Viscosity(mPa·S(25℃)) |
5000-8000 |
|
Lonicity |
Non-ionic |
|
Solvent |
Water or environmental hydrophilic solvent |
Character
1.Free of toluene, organotin, APEO, and other toxic substances;
2.Nonionic, performance is not affected by the pH of the system;
3.No adverse effects on the gloss of formulated products
Usage and dosage
Can be added at the grinding or paint mixing stage or after adding the emulsion. It is recommended to add 0.5-3% (of the total formula). The exact amount added should be determined based on different formulas and required viscosity. For better dispersion and to avoid lumping, it should be diluted with water or solvent before adding in a ratio of 1:1.
Notes
Associative thickening is affected by temperature. At low temperatures, the viscosity is higher, while at high temperatures, it is lower. The temperature conditions should be considered when designing the formula;
When the batch of thickened raw materials changes, the experiment should be repeated to determine the amount of thickener;
Its own viscosity has temperature effects, so it is easy to pump above 20℃.
Storage and expiration
It can be stored in its original closed packaging within the temperature range of 5℃～35℃for one year.
Package
125Kg、50KG/Drum
JLY-Z50 is an non-ionic polyether type polyurethane associative thickener(HEUR),endows the system with a false plastic condition.It provide effect thickening property in the low and middle share speed
JLY-1272HS is waterborne environmental polyurethane resin polyurethane binder for production of water-based gravure surface or lamination printing ink with good grindability and pigment dispersibility
polyurethane resin is widely used for production of coating&paint, ink ,adhevise etc,and good adhesion on papper、leather、fabric、glass and plastic substrate with flexibility and wear resistance
JLY-103 as a high-temperature boiling resistant polyurethane resin with excellent dispersion performance for carbon black, especially suitable for the production of high-speed film gravure reverse printing pigment and black ink
Polyurethane dispersions are important materials used in the preparation of screen printing inks for the textile industry. They serve as binders that provide adhesion and cohesion to the ink, ensuring that it adheres well to the substrate and maintains its shape during the printing process.tc
Polyurethane resin has several advantages in the preparation of flexo printing ink. Firstly, it can improve the hardness and scratch resistance of the ink, making it more durable and resistant to wear and tear. Secondly, polyurethane resin can enhance the adhesion of the ink to different substrates, resulting in better print quality and colorfastness. Thirdly, it can provide a smoother and glossier finish to the printed material, which is particularly important for high-end applications such as packaging and labeling. Finally, polyurethane resin can also increase the chemical resistance of the ink, making it suitable for use in harsh environments or with aggressive solvents. Overall, the use of polyurethane resin in flexo printing ink formulations can lead to improved performance and increased value for customers.
S-6961-1 is excellent Bonding Strength Polyurethane PU Resin for Printing ink.It's as one of forming-film polyurethane binder for production of gravure printing ink
Polyurethane dispersions (PUDs) are water-based polymeric materials that find wide application across various industries, including the production of gloves. PUDs are known for their excellent film-forming properties, high elasticity, and good mechanical strength. They are commonly used as coating materials in glove manufacturing due to their desirable properties, such as flexibility, durability, and resistance to abrasion.
IPv6 network supported
English
русский
español
português
العربية
日本語
한국의
Türkçe
ไทย
हिंदी
Indonesia 